(Summary description)1.Thebasicstructureoftheplasticmodifiedgranulator:1.Twin-screwmainengine2.Waterstretchhead3.Conveyorbelt4.Pelletizer5.Silo  2.Basicintroductionofplasticmodifiedgranulatoroftwinscrewgranulator:   Thetwin-screwgranulatorhasagoodplasticizingeffectonthematerialthroughtheshearingcombinationofmanyscrewblocks,andcanbesuitableforvariousmaterialsbychangingthecombinationofscrewelements.

新闻

Introduction to plastic modified granulator

Introduction to plastic modified granulator

新闻

Introduction to plastic modified granulator

(Summary description)1.Thebasicstructureoftheplasticmodifiedgranulator:1.Twin-screwmainengine2.Waterstretchhead3.Conveyorbelt4.Pelletizer5.Silo  2.Basicintroductionofplasticmodifiedgranulatoroftwinscrewgranulator:   Thetwin-screwgranulatorhasagoodplasticizingeffectonthematerialthroughtheshearingcombinationofmanyscrewblocks,andcanbesuitableforvariousmaterialsbychangingthecombinationofscrewelements.

  • Categories:Industry News
  • Author:
  • Origin:
  • Time of issue:2020-07-17 16:31
  • Views:
Information
1. The basic structure of the plastic modified granulator: 1. Twin-screw main engine 2. Water stretch head 3. Conveyor belt 4. Pelletizer 5. Silo
 
 
2. Basic introduction of plastic modified granulator of twin screw granulator:
      The twin-screw granulator has a good plasticizing effect on the material through the shearing combination of many screw blocks, and can be suitable for various materials by changing the combination of screw elements.

Scan the QR code to read on your phone

Previous: None
Next: About the deceleration principle of double screw extruder
Previous: None
Next: About the deceleration principle of double screw extruder
About the structure process analysis of twin screw extruder

About the structure process analysis of twin screw extruder

Next,theeditorofJuliwillgiveyouabriefintroductionaboutthestructureandprocessanalysisofthetwin-screwextruder:  1.Plasticizingarea  Theplasticizingzoneistoheattheinjectedresintoformamoltenstate.Theconditionssuchastheheatingtemperatureandtimeinthisregionarenotparticularlylimitedaslongasthefluoropolymerhavingaspecificunstableterminalgroupisinamoltenstate.Inthelatterhalfoftheplasticizationzone,itispreferabletoprovidedevolatilizationholestoremoveatleastapartofvolatilecomponentsundernormalpressureorreducedpressure.Then,thepartialpressureofvolatilecomponentsinthestabilizationregiondescribedlatercanbereduced,andthestabilizationtreatmentcanbeeffectivelypromoted.  2.Stabilizationtreatmentarea  ThestabilizationzoneistomeltandkneadandconvertspecificunstableendgroupsintoaCF2H.Thestabilizationtreatmentareaispreferablyformedbyusingakneadingdiscwithoutpropulsion.Here,melt-kneadingiscarriedoutinthepresenceofwaterandoxygen.Itcandirectlyintroducepurewater,ionexchangewater,etc.orwatervapor;itcanalsobeaccompaniedbythefluoropolymertobetreated.Theamountofwateraddedisthesameasthenumberofunstableterminalgroups,butitisactuallypreferabletosupplyanexcessamount,forexample,atleast10timestheamount.Thepressureinthestabilizationzoneisgenerallycontrolledat0.2～10MPa,andthesettemperatureiscontrolledat280～430℃.Thetimetomaintainpressurizationisusuallylessthan10minutes.  Accordingtotheprincipleoftheextrudertoremoveunstableendgroups,themelt-kneadinginthestabilizationzoneispreferablycarriedoutinthepresenceofoxygeninadditiontothepresenceofwater.Airisusuallyusedintermsofeconomy.Inthepresenceofoxygen,thecarbongeneratedbythemoltenkneadedproductisalsoburned,whichcaninhibitthecoloringofthefluoropolymer.Oxygenisaninertgastotheunstableterminalgroupscarboxylandfluorinatedacylgroups.Duringtheprocessofmeltingandkneading,itcanimprovethedevolatilizationefficiencyofvolatilecomponents.  Three,devolatilizationarea  Thedevolatilizationzoneremoveshigh-temperaturevolatilecomponentsgeneratedbythedecompositionofspecificunstableterminalgroups.Theabsolutepressurevariesaccordingtothemoltenstateofthemoltenkneadedproductandtheoperatingconditionsofthescrewofthekneader.Generally,thepressureisreducedtothepointwherethemoltenkneadedproductdoesnotintrudeintotheexhaustnozzle.Itcanbe0.01to0.1MPa,andthetemperatureiscontrolledat25O~Claughataround.  Inthepresenceofacertainamountofwaterandoxygen,FEPextrudingthroughatwin-screwextrudercaneffectivelyremovetheunstableterminalgroupsofFEP.SimplifiestheprocessingprocessofFEPunstableendgroupsandsavesproductioncosts.Whentheobtainedstabilizedpolymerismelt-formed,nobubblesorvoidsaregeneratedinthefinishedproduct,anditisnotcolored. Formoreinformationabouttwinscrewextruders,pleasevisithttp://www.njjl.com/
发布时间 : 2020-07-30 点击 : 0
What are the technical parameters of a single screw extruder

What are the technical parameters of a single screw extruder

Next,theeditorofJuliwillgiveyouabriefintroductionaboutthetechnicalparametersofthesinglescrewextruder? 1.Screwdiameter:referstothediameteroftheoutercircleofthescrew,representedbyD,andtheunitismillimeter(mm).2.Screwlength-to-diameterratio:referstotheratioofthelengthLoftheworkingpartofthescrew(thelengthofthethreadedpart,thatis,thelengthfromthecenterlineofthefeedingporttotheendofthescrew)andthescrewdiameterD,expressedbyL/D.3.Rangeofscrewrotationspeed:referstothemaximumrotationspeedofthescrewtotheminimumrotationspeedofthescrew;nrepresentsthescrewrotationspeed,andtheunitisrevolutionsperminute(r/min).HuahongAnswer4.Powerofthedrivingmotorofthemainscrew:ExpressedbyP,theunitiskilowatt(kW).5.Heatingpowerofextruderbarrel:ExpressedbyE,theunitiskilowatt(kV).6.Theproductioncapacityoftheextruder:expressedbyQ,theunitiskilogramperhour(kg/h).7.Theheightofthecenteroftheextruder:referstothedistancefromthecenterlineofthescrewtotheground,expressedbyH,andtheunitismillimeter(mm).8.Externaldimensionsoftheextruder:referstothetotallength×totalwidth×totalheight,expressedbyL×W×H,andtheunitismillimetersormeters(mmorm)9.Extruderquality:expressedbyW,theunitiskilogramorton(kgort)
发布时间 : 2020-07-30 点击 : 0
Two more effective cleaning agents for starting the double screw extruder

Two more effective cleaning agents for starting the double screw extruder

Next,Iwillgiveyouabriefintroductiontotwomoreeffectivecleaningagentsforstartingthedoublescrewextruder:    1.Mixture:50%HDPE+50%diatomaceousearth    2.Mixture:HDPE+water+decontaminationpowder.TheHDPEisfedintothescrewattheusualspeedatthemeltingtemperature.Stirthedecontaminationpowderwithwaterinabuckettoformaslurry,andslowlyaddtheslurryfromthemainfeedport.Theseslurriesimpact,rub,andcleanthescrewduetofoaming.    Formoreinformationabouttwinscrewextruders,pleasevisithttp://www.njjl.com/
发布时间 : 2020-07-30 点击 : 0

CONTACT INFORMATION

No. 77 Tangtong Road / No. 9 Boguang Road, Hushu Town, Jiangning District, Nanjing City

OFFICIAL ACCOUNTS

Welcome to follow us

er

ONLINE MESSAGE

Username used for comment:
客户留言
Description:
验证码

Copyright © 2020 Nanjing Juli Chemical Machinery Co., Ltd. All Rights Reserved. 苏ICP备13041019号-2  Powered by www.300.cn